卤胺抗菌棉织物的制备及性能研究

作者信息 +

Research on preparation and property of N-halamine treated antibacterial cotton fabric

Zheng Yuxia, Li Xia, Liu Ying, Ren Xuehong

Author information +

文章历史 +

Received		Published
2020-06-02		2021-10-20
Issue Date	Revised Date
2021-11-02	2020-06-02

PDF

摘要

利用卤胺载体氯化三甲基铵乙酰肼(GT)与三聚氯氰(CYCH)间的亲核反应,制得二氯三嗪类卤胺抗菌前驱体2,4-二氯-6-(乙酰氨基-胺基)三甲基氯化铵-1,3,5三嗪(DTCT)。经低温活性染料染色工艺将DTCT接枝到棉织物上,氯化得到了新型抗菌棉织物(Cotton/DTCT-Cl)。通过红外光谱、扫描电镜验证了抗菌棉织物的成功制备。研究了整理前后棉织物的断裂强力及氯化后织物的抗菌效果。综合各项测试发现,此方法在保证高效抗菌的同时较好地保留了织物的力学性能。

Abstract

Novel kind of dichlorotriazine N-halamine antibacterial precursor 2,4-dichloro-6-(acetamino-amine) trimethylammonium chloride-1,3,5 triazine (DTCT) was prepared by the nucleophilic reaction between Girad's reagent T (GT) and cyanuric chloride (CYCH).The DTCT compound was grafted onto cotton fabric through the finishing process of active dyestuff at low temperature,and the antibacterial cotton fabric was prepared after chlorination processing.The successful preparation of the grafted fabric was determined by analyzing the FT-IR and SEM images.The breaking strength of different fabrics and the bactericidal efficacy of chlorinated DTCT treated cotton fabric were studied as well.Taking into account all the results,the finishing method can not only guarantee the effective antibacterial effect but also retained the mechanical properties of the fabric.

关键词

抗菌剂 / 制备 / 整理工艺 / 性能检测

Key words

antibacterial agent / preparation / finishing process / performance examination

引用本文

引用格式 ▾

卤胺抗菌棉织物的制备及性能研究[J]. 化工新型材料, 2021, 49(10): 165-169 DOI:10.19817/j.cnki.issn 1006-3536.2021.10.035

登录浏览全文

4963

注册一个新账户忘记密码

参考文献

原文顺序 | 出版日期 | 本文引用

[1] 王济永.可持续发展的棉织物染整加工技术[J].纺织导报,2009(10):52-63.
[2] Worley S D,Chen Y,Wang J W,et al.Novel N-halamine siloxane monomers and polymersfor preparing biocidal coatings[J].Surface Coatings International Part B:Coatings Transactions,2005,88(2):93-99.
[3] Kocer Hasan B,Cerkez Idris,Worley S D,et al.Polymeric antimicrobial N-halamine epoxides[J].ACS Applied Materials & Interfaces,2011,3(8):2845-2850.
[4] 汪怿翔,张俐娜.天然高分子材料研究进展[J].高分子通报,2008(7):66-76.
[5] 马志鹏,丁放,林兴焕,等.电子束辐照制备卤胺抗菌棉织物[J].辐射研究与辐射工艺学报,2018,36(4):33-37.
[6] 赵静,邓桦,李海霞.纳米氧化锌抗紫外和抗菌棉织物[J].印染,2009,35(8):19-21.
[7] Jiang Z M,Liu Y,Li R,et al.Preparation of antibacterial cellulose with a monochloro-s-triazine-based N-halamine biocide[J].Polymers for Advanced Technologies,2015,27:460-465.
[8] 蒋之铭,朱平,任学宏,等.基于三聚氯氰的反应型抗菌剂及其抗菌整理研究[J].现代化工,2017,37(6):107-111.
[9] Yan Z,Xue W L,Zeng Z X,et al.Kinetics of cyanuric chloride hydrolysis in aqueous solution[J].Industrial & Engineering Chemistry Research,2008,47(15):5318-5322.
[10] Liu Y,Ma K K,Li R,et al.Antibacterial cotton treated with N-halamine and quaternary ammonium salt[J].Cellulose,2013,20(6):3123-3130.
[11] Liu Y,He Q H,Li R,et al.Durable antimicrobial cotton fabrics treated with a novel N-halamine compound[J].Fibers and Polymers,2016,17(12):2035-2040.
[12] 赵涛.染整工艺与原理[M].北京:中国纺织出版社,2009:65-72.
[13] 蒋之铭,任学宏.棉织物的三嗪类卤胺化合物抗菌整理[J].印染,2014(23):15-18,50.
[14] Murugan E,Gopinath P,Shanmugayya V,et al.Antibacterial activity of novel insoluble bead-shaped polymer-supported multiquaternary ammonium salts[J].Journal of Applied Polymer Science,2010,117:3673-3678.
[15] Sun Y Y,Sun G.Synthesis,characterization,and antibacterial activities of novel N-halamine polymer beads prepared by suspension copolymerization[J].Macromolecules,2002,35:8909-8912.
[16] Chen Z B,Luo J,Sun Y Y.Biocidal efficacy,biofilm-controlling function,and controlled release effect of chloromelamine-based bioresponsive fibrous materials[J].Biomaterials,2007,28(9):1597-1609.